Насосing and conveying coagulation construction has become one of the main construction methods. During the pumping process, it is sometimes found that the slump of the concrete entering the pump is normal, but the slump loss after pumping is serious, and even does not meet the construction requirements. This phenomenon is called "slump pumping loss".

Concrete pump loss is a phenomenon produced by concrete under the action of pumping pressure, which is difficult to find with the current commonly used detection methods.

At present, the method of detecting concrete mixture in the construction process is mainly the slump method. The slump method is a reflection of the natural flow of the concrete mixture. It is difficult to find out whether the concrete mixture will have pump loss. The reason is that the current test methods are difficult to reflect the change of concrete workability under the concrete pressure state.

If the concrete mixture wants to flow, it must be driven by liquid water, and the mortar drags the stones to flow, that is, the surface of the solid material is lubricated by liquid water and pushed to flow, and the tiny gaseous bubbles show a "ball" effect, which is beneficial to slurry flow.

Бетон-это трехфазная смесь твердого, жидкости и газа. Из -за разницы в плотности и состоянии твердое вещество, жидкость и газ будут показывать различные изменения под давлением. Этот вид разделения является своего рода динамическим разделением с внешней силой, которая отличается от статического разделения, и метод спада не может отражать это состояние разделения. уменьшенный. Бетонное спад уменьшается. Сокращение пузырьков воздуха приведет к исчезновению эффекта «шарика», а бетонная смесь также будет разрушаться. По этим причинам феномен потери насоса может контролироваться путем контроля свободного содержания воды и содержания воздуха в бетонной смеси. Преодоление явления потери насоса состоит в том, чтобы сохранить свободную воду во время процесса накачки и поддерживать толщину водной пленки на поверхности твердой фазы бетонной смеси.

The difference in the movement speed of each component of the concrete mixture under the pumping pressure will cause a certain component of the mixture to separate when it encounters an elbow or a joint. This kind of separation is a kind of dynamic separation with external force, which is different from static separation, and the slump method cannot reflect this separation state.

Pressure effect When the aggregate has many voids and the water absorption rate is too large, the pump pressure can increase and accelerate the water absorption rate of the aggregate, causing free water in the mixture to enter the inside of the aggregate, and the free water in the mixture is reduced. Concrete slump is reduced.

Secondly, under the action of pumping pressure, the tiny air bubbles in the concrete mixture will be deformed or even burst. The reduction of the air bubbles will cause the "ball" effect to disappear, and the concrete mixture will also collapse.

The above reasons may be the cause of pump loss. For these reasons, the pump loss phenomenon may be controlled by controlling the free water content and air content of the concrete mixture.

Under the pumping pressure of the concrete mixture, the free water migrates obviously, and the free water is separated from the concrete mixture, resulting in a decrease in the free water of the concrete mixture and a decrease in the fluidity of the mixture.

Therefore, the essence of overcoming the pump loss phenomenon is to keep its free water during the pumping process and maintain the thickness of the water film on the surface of the solid phase of the concrete mixture.

Вода в бетонной смеси разделена на три части, одной частью является вода, необходимая для гидратации цемента, вторая - это вода, поглощаемая заполнителем, а последняя - свободная свободная вода в смеси. Свободная вода является движущей силой для обслуживания бетонной смеси. . Отрегулируйте совместимость примеси в бетонной смеси, улучшите удержание воды и текучесть бетонной смеси, и не подходит для уменьшения количества восстановителя воды, удерживающего ликер и спада, в примеси. || 286

Minimize the consumption of free water during pumping pressure to control slump.

During the pumping process, to maintain the amount of free water, the following suggestions can be used as a reference:

1. Adjust the compatibility of the admixture in the concrete mixture, improve the water retention and fluidity of the concrete mixture, and it is not appropriate to reduce the amount of water reducer mother liquor and slump retaining agent in the admixture.

2. Improve the quality of concrete aggregates, avoid the use of aggregates with many pores and high water absorption, and pay special attention to avoiding the use of aggregates with large mud content and flocculants.

3. Оптимизируйте агрегатную графику, уменьшите соотношение пустоты агрегата и уделяйте приоритет использования грубых и мелких агрегатов с лучшей формой частиц.

4. Добавьте определенное количество агента с воздуха, стабилизатора пены или ингибитора пены в примеси, чтобы уменьшить потерю пузырьков воздуха в бетонной смеси во время накачки. || 289

5. During the concrete pouring process, try to avoid the phenomenon of rolling, waiting for a long time, it is easy to cause the loss of concrete slump, the deterioration of fluidity, and the induction of pump loss.

6. Отрегулируйте количество примесей в соответствии с состоянием бетонной смеси и постарайтесь избежать плохой текучести бетона, что обычно показывает, что смесь имеет спад, но нет расширения, плохого динамического ощущения и «мертвого серого».

7. Температура цемента высока, а скорость гидратации быстрая. Увеличьте количество примесей как можно больше, чтобы избежать недостаточной примеси, высокого потребления воды и плохого задержки бетона воды. || 292

8. Pay attention to check the sealing condition of the sealing ring at the pump pipe joint to ensure no air leakage or slurry leakage.

Other factors that cause concrete "pump loss":

1. The specific surface area of cement is large, and the cement particles are fine. Under the pumping pressure, the hydration of the particles will be accelerated, and more flocculent substances will be formed, which will affect the fluidity.

2. Потеря воспламенения минеральной примеси слишком велика, а вещество с высокой скоростью поглощения воды имеет большое содержание. Под действием давления насоса свободная вода быстро входит в вещество

3. Скорость поглощения воды в заполнителе слишком высока, потому что отверстия или трещины на поверхности заполнителя заставляют некоторую воду проникать под давлением, а даже некоторые твердые частицы примеси попадают в поры и влияют на эффективность примесей. Здесь он также включает в себя явление сниженной подвижности.

4. Качество компонента воздуха в примеси не очень хорошо. Он должен быть стабильным и маленьким пузырьками, но пузырьки, которые слишком большие и не стабильные, будут разрываться под действием давления и потеряют эффект «смазывания»;

5. Бетон транспортируется на большем расстоянии, и чем больше горизонтальное расстояние переноса, тем более склонным к потере насоса, особенно летом, когда температура смеси высока, воздействие на его текучесть больше. накачиваемость.

The method of judging that the concrete mixture may have pump loss:

Observe the water retention and cohesion of concrete mixing, test the slump, expansion, and flow rate slump, and judge the pumpability.

Например, во время теста на спад бетон не течет быстро после того, как цилиндр спада поднимается, что указывает на то, что текучесть не очень хороша;

Если бетонная смесь устарела, дивергентно и плохая в сплоченном виде, это означает, что это не подходит для насыпной ссоры. Плохое задержку воды, а суспензия и вода легко разделяются путем перекачки. Состояние кровотечения бетона под давлением может отражать способность бетона за удержание воды под давлением.

Slurry bleeding and layered bottoming of the concrete mixture indicate poor water retention, and the slurry and water are easily separated by pumping.

The current use of the slump method cannot effectively reflect the pump loss phenomenon under the pumping pressure. The bleeding state of the concrete under the pressure can reflect the water retention capacity of the concrete under the pressure.

Производительность кровотечения давления бетонной смеси - это скорость кровотечения давления, а это процент бетонной смесью кровотечения в течение определенного времени под определенным давлением. Как правило, относительная скорость кровотечения давления накачанного бетона в течение 10 секунд не должна превышать 40 %. Запрос